SHT Preshaed Dental Zirconia Blocks
SHT
Translucency 45%
Strength 1100 Mpa
Thickness: 10mm/12mm/14mm/16mm/18mm/20mm/22mm/25mm/30mm
Strength 1100 Mpa
Thickness: 10mm/12mm/14mm/16mm/18mm/20mm/22mm/25mm/30mm
Delivery
FOB
minimum order
1 piece
Supply Ability
10000piece / Month
Stock Time
7Day
Quantity
Super High Translucency SHT Multilayer zirconia(Well-balanced Translucency and Strength)
Vsmile SHT Multilayer Zirconia Disc is a dental multilayer zirconium oxide(4Y-TZP ) with natural color gradient and high flexural strength (1100MPa). These properties enable the fabrication
of highly esthetic, monolithic single-tooth and bridge restorations in the anterior and posterior regions. The specially adjusted translucency gradient ensures good coverage in the cervical
area and increased translucency in the incisal area. The integrated color gradient also ensures the efficient fabrication of natural-looking restorations.
Vsmile SHT Multilayer Zirconia Milling Disc is the best material to get a perfect result for Full-Contour-Zirconia solutions.
Vsmile SHT Multilayer Zirconia Milling Disc is the best material to get a perfect result for Full-Contour-Zirconia solutions.
Processing Options
Monolithic processing or partial ceramic veneering
Indications
- Single-tooth restorations (anterior with esthetics and posterior with good strength)
- 3-unit bridges (anterior and posterior)
- Multi-unit bridges (anterior and posterior)
- Veneer
Model
- 98mm (10mm, 12mm, 14mm, 16mm, 18mm, 20mm, 22mm, 25mm 30mm) For Open System
- 71mm (10mm, 12mm, 14mm, 16mm, 18mm, 20mm, 22mm, 25mm, 30mm) For Amann Girrbach CERAMILL CAD/CAM SYSTEM
- 95mm (10mm, 12mm, 14mm, 16mm, 18mm, 20mm, 22mm, 25mm, 30mm) For Zirkonzahn CAD/CAM SYSTEM
Colors
Vita 16 Shades, Bleach colors BL1/BL2/BL3/BL4
Sintering Temperature
Max. Temp. 1500℃
Parameters
| Properties | SHT |
| Density before sintering(g.cm-3) | 3.15±0.05 |
| Density after sintering（g.cm-3） | 6.08±0.01 |
| CTE(25-500℃)(K-1) | （10.5±0.5）×10-6 |
| Flexural strength after sintering(Mpa) | 1100 |
| Translucency(1.0±0.02mm) | 46% |
| Fracture toughness(MPa.m1/2) | 5.7 |
| Hardness(HV10) | 1300 |
| Accelerated aging surface monoclinic phase content | ＜5% |
| Chemical solubility after sintering(μg.cm-2) | ＜100 |
| Cytotoxicity | 0 Level |
| Radioactivity(Bq.g-1) | ＜0.1 |
| Sintering temperature(℃) | 1500-1530 Recommend 1500 |
Client Case： Full mouth veneer with ceramic, anterior, single crown and 3-unit bridge